| Properties | Value |
|---|---|
| Chemical Analysis (in %) | |
| O | 0.4 max. |
| Fe | 0.3 max. |
| C | 0.01 max. |
| N | 0.05 max. |
| H | 0.0125 max. |
| Ti | > 99.0 |
| Mechanical Properties | |
| Tensile strength | 680 MPa min. |
| Elongation | 10% |
| E-Modul | 110 GPa |
Material
Titanium Grade 4
Titanium Ti6Al4V
| Properties | Value |
|---|---|
| Chemical Analysis (in %) | |
| Al | 5.5 – 6.75 max. |
| V | 3.5 – 4.5 max. |
| Fe | 0.3 max. |
| C | 0.08 max. |
| N | 0.05 max. |
| H | 0.015 max. |
| Ti | ~ 90 |
| Mechanical Properties | |
| Tensile strength | 860 MPa min. |
| Elongation | 10% |
| E-Modul | 110 GPa |
HMA castable alloy
| Properties | Value |
|---|---|
| Chemical Analysis (in %) | |
| Au | 60 |
| Pt | 19 |
| Pd | 20 |
| Ir | 1 |
| Mechanical Properties | |
| Density | 17.5 g/cm³ |
| Colour | white |
| WAK | 12.5 (20-500 °C) 12.6 (20-600 °C) |
| E-Modul | 136 GPa |
| Hardness HV | 240 (700°C / 30 min.) |
| 0.2%-Elongation limit | 610 |
| Fracture strain | 17% |
| Tensile strength | 770 MPa |
Au-Pt alloy
| Eigenschaft | Value |
|---|---|
| Chemical Analysis (in %) | |
| Au | 70.0 |
| Pt | 8.5 |
| Ag | 13.4 |
| Zn | 0.5 |
| Cu | 7.5 |
| Ir | 0.1 |
| Mechanical Properties | |
| Density | 16.0 g/cm³ |
| Colour | yellow |
| E-Modul | 100 GPa |
| Hardness HV | 136 GPa |
| Hardness HV | annealed: 170 hardened: 295 self hardened: 240 |
Zirconium oxide
| Properties | Value |
|---|---|
| Chemical Analysis (in %) | |
| Zirconium oxide (ZrO2 + HfO2) | 94 |
| Yttrium oxide (Y2O/sub>3) | 5 |
| Aluminum oxide (Al2O3) | < 1 |
| Mechanical Properties | |
| Density | > 6.06 g/cm³ |
| Porosity open | 0 % |
| Colour | white / x-ray opaque |
| WAK | 10.10-6 / K (25 – 500°) |
| E-Modul | 210 GPa |
| Hardness HV | max. 1290 |
| Tensile strength | 2000 MPa |
| Transversal strength (4-point) | 950 MPa |
| Fracture touchness | 7 MPa*m1/2 |